Stress Distribution in Co-Cr Implant Frameworks after Laser or TIG Welding

Lack of passivity has been associated with biomechanical problems in implant-supported prosthesis. The aim of this study was to evaluate the passivity of three techniques to fabricate an implant framework from a Co-Cr alloy by photoelasticity. The model was obtained from a steel die simulating an edentulous mandible with 4 external hexagon analog implants with a standard platform. On this model, five frameworks were fabricated for each group: a monoblock framework (control), laser and TIG welding frameworks. The photoelastic model was made from a flexible epoxy resin. On the photoelastic analysis, the frameworks were bolted onto the model for the verification of maximum shear stress at 34 selected points around the implants and 5 points in the middle of the model. The stresses were compared all over the photoelastic model, between the right, left, and center regions and between the cervical and apical regions. The values were subjected to two-way ANOVA, and Tukey's test (α=0.05). There was no significant difference among the groups and studied areas (p>0.05). It was concluded that the stresses generated around the implants were similar for all techniques.

Resumo A falta de passividade tem sido associada a problemas biomecânicos em próteses implantossuportadas. A proposta deste estudo foi avaliar, por meio da fotoelasticidade, a influência de três diferentes de fabricação de infraestrutura em liga de Co-Cr na passividade destas. O modelo foi obtido a partir de uma matriz de aço simulando uma mandíbula edêntula com 4 análogos de implantes de hexágono externo com plataforma padrão. Neste modelo, foram confeccionados cinco amostras para cada grupo: infraestruturas em monobloco, infraestruturas soldadas a laser e soldadas a TIG. O modelo fotoelástico foi feito com uma resina epóxi flexível (GIII, Polipox Industria e Comercio Ltda.). Na análise fotoelástica, as infraestruturas foram aparafusadas no modelo para a verificação da tensão de cisalhante máxima em 34 pontos selecionados ao redor dos implantes e 5 pontos na região média do modelo. Foram comparadas as tensões em todo o modelo fotoelástico, entre as regiões direita, esquerda e centro e também entre as regiões cervical e apical. Os valores foram submetidos à análise de variância a dois critérios, seguido pelo teste de Tukey (α=0,05). Os resultados não mostraram diferença significativa entre as tensões presentes nos grupos e nas áreas estudadas. Conclui-seque as tensões geradas ao redor dos implantes foram semelhantes entre as diferentes técnicas de confecção e entre todas as regiões analisadas. .

Effect of plasma welding parameters on the flexural strength of ti-6al-4v alloy

The aim of this study was to assess the effect of different plasma arc welding parameters on the flexural strength of titanium alloy beams (Ti-6Al-4V). Forty Ti-6Al-4V and 10 NiCr alloy beam specimens (40 mm long and 3.18 mm diameter) were prepared and divided into 5 groups (n=10). The titanium alloy beams for the control group were not sectioned or subjected to welding. Groups PL10, PL12, and PL14 contained titanium beams sectioned and welded at current 3 A for 10, 12 or 14 ms, respectively. Group NCB consisted of NiCr alloy beams welded using conventional torch brazing. After, the beams were subjected to a three-point bending test and the values obtained were analyzed to assess the flexural strength (MPa). Statistical analysis was carried out by one-way ANOVA and Tukey's HSD test at 0.05 confidence level. Significant difference was verified among the evaluated groups (p<0.001), with higher flexural strength for the control group (p<0.05). No significant differences was observed among the plasma welded groups (p>0.05). The NCB group showed the lowest flexural strength, although it was statistically similar to the PL 14 group (p>0.05). The weld depth penetration was not significantly different among the plasma welded groups (p=0.05). Three representative specimens were randomly selected to be evaluated under scanning electron microcopy. The composition of the welded regions was analyzed by energy dispersive X-ray spectroscopy. This study provides an initial set of parameters supporting the use of plasma welding during fabrication of titanium alloy dental frameworks.

O objetivo deste estudo foi avaliar o efeito de diferentes parâmetros de solda a plasma verificando a resistência flexural de barras de liga de titânio (Ti-6Al-4V). Quarenta espécimes de Ti-6AL-4V e dez espécimes de liga de NiCr foram preparados (40 mm de altura e 3,18 mm de diâmetro) e divididos em 5 grupos (n=10). As barras de liga titânio do grupo controle não foram seccionadas e nem submetidas a processo de soldagem. Os grupos PL10, PL12 e PL14, continham barras de titânio seccionadas e soldadas com uma corrente de 3 A por períodos de 10,12 e 14 ms, respectivamente. O grupo NCB consistiu de barras de liga de NiCr soldadas pelo método de brasagem convencional. Em seguida as barras foram submetidas ao teste de flexão de três pontos e os valores obtidos foram transformados em resistência flexural (MPa). Análise estatística foi realizada usando ANOVA de fator único e o teste Tukey com o nível de significância de 0,05. Diferença estatística foi verificada entre os grupos avaliados (p<0,001), com os maiores valores pra o grupo controle. Não foram encontradas diferenças entre os grupos de solda plasma (p>0,05). O grupo NCB apresentou os menores valores de resistência flexural embora tenha sido estatisticamente semelhante ao grupo PL14. Não houve diferença significante na profundidade de penetração entre os grupos de solda plasma (p=0,05). Três espécimes representativos foram aleatoriamente selecionados para serem avaliados por meio de microscopia eletrônica de varredura. A composição das regiões soldadas foi verificada por meio de espectroscopia por energia dispersiva. Este estudo fornece informações iniciais de parâmetros para permitir a utilização de soldagem plasma durante a fabricação de estruturas em liga de titânio.